Influence of heating temperature and holding time on biochars derived from rubber wood sawdust via slow pyrolysis

Se, Sian Meng and Shaaban, Azizah and Dimin @ Mohd Amin, Mohd Fairuz and Mohamad Juoi, Jariah and Mohd Husin, Mohd Haizal and Mitan, Nona Merry Merpati (2014) Influence of heating temperature and holding time on biochars derived from rubber wood sawdust via slow pyrolysis. Journal of Analytical and Applied Pyrolysis, 107. 31- 39. ISSN 0165-2370

Text Influence of heating temperature and holding time on biochars derived from rubber wood sawdust via slow pyrolysis.pdf Restricted to Registered users only Download (2MB) | Request a copy

Abstract

Biochar samples were produced from rubber wood sawdust (RWSD), which is a by-product from sawmills, via slow pyrolysis. Biochar is a potential additive for agricultural soil as a soil amendment and for agronomics. The approach proposed in the current study considers the effects of heating temperature and holding time on the surface functional groups and morphologies of RWSD-derived biochars. The pyrolysis was performed in a vertical tube furnace heated at 5 °C/min from room temperature to maximum heating temperatures of 300 °C, 400 °C, 500 °C and 700 °C under nitrogen gas purging at a rate of 30 ml/min. Two sets of biochars were produced with holding times of (i) 1 h and (ii) 3 h. Proximate and ultimate analyses were performed on the raw RWSD using thermogravimetric analysis (TGA) and carbon-hydrogen-nitrogen (CHN) elemental analysis. The influence of heating temperature and holding time on biochar surface functional groups and porosities was investigated using X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, Boehm titration, pH alkalinity, Brunauer-Emmett-Teller (BET) surface area analysis, scanning electron microscopy (SEM) and SEM with energy-dispersive X-ray (SEM-EDX) spectrocopy. The FT-IR spectra indicated the presence of acidic functional groups, such as carboxylic, phenolic and lactonic groups, and these groups were quantified by Boehm titration. The number of acidic functional groups decreased as the heating temperature and holding time increased. The maximum amount of acidic functional groups was determined to be 1.9 mmol/g at 300 °C for a 1-h holding time compared to 1.3 mmol/g for a 3-h holding time and 1.0 mmol/g with a 1-h holding time at 700 °C. All of the biochars produced at heating temperatures above 400 °C were alkaline, and the pH value increased as the heating temperature and holding time increased. The biochar produced at 300 °C with a 1-h holding time had a pH of 6.72 and the sample produced with a 3-h holding time had a pH of 7.67. In addition, the sample produced when the temperature was increased to 700 °C with a 1-h holding time had a pH of 11.44. The BET surface area analysis reported maximum values of 5.49 m2/g, and the total pore volume was 0.0097 cm 3/g at a heating temperature of 700 °C with a 3-h holding time. SEM micrographs clearly showed the development of well-defined pores in the biochars, and the SEM-EDX spectra indicated localised carbon and oxygen content in all the samples. The results indicated that biochars produced from RWSD are potentially beneficial as soil amendments. However, an extensive study of biochar sustainability is worth investigating.

Item Type:	Article
Uncontrolled Keywords:	Rubber wood sawdust, Slow pyrolysis, Biochar, Surface functional groups, BET specific surface area
Subjects:	T Technology > TA Engineering (General). Civil engineering (General)
Divisions:	Faculty of Manufacturing Engineering > Department of Manufacturing Process
Depositing User:	Mr Mohd Fairuz Dimin
Date Deposited:	19 Nov 2014 01:28
Last Modified:	04 Jul 2023 11:20
URI:	http://eprints.utem.edu.my/id/eprint/11713
Statistic Details:	View Download Statistic

Actions (login required)

View Item