Bimetallic Nanoparticles Pt–M (M=Cu, Fe, or Ni) Preparation Based on Modified Polyol Method for N2O decomposition activity

Mohd Husin, Mohd Haizal and Kong Yong, Liew and Sim Yee , Chin and Mohd Ridzuan, Nordin (2010) Bimetallic Nanoparticles Pt–M (M=Cu, Fe, or Ni) Preparation Based on Modified Polyol Method for N2O decomposition activity. In: Malaysian Technical Universities Conference on Engineering and Technology , 28-29, June , 2010, Bayview Hotel, Melaka, Malaysia.

[img] Microsoft Word
PtM_mucet2010.doc
Restricted to Registered users only

Download (2MB) | Request a copy

Abstract

Pt-M (M = Cu, Fe, or Ni) bimetallic nanoparticles were synthesized by modified polyol method using ethylene glycol (EG) as the solvent and PVP as the stabilisation agent with reduction by using NaBH4 at room temperature. The samples were characterised by transmission electron microscopy (TEM) and analyses confirm that the very fine and monodisperse with narrow size distribution particle with average particle size were 3.1 ± 1.0 nm for Pt-Cu, 4.2 ± 1.3 nm for Pt-Fe and 3.9 ± 1.5 nm for Pt-Ni. XRD results show that there is no peak in the pattern of bimetallic nanoparticles observed unless peak of alumina refer to gamma alumina support. Catalytic decomposition of nitrous oxide over alumina supported Pt based bimetallic testing revealed the enhancing of catalytic activity, when Pt-Cu shows the highest N2O decomposition activity of almost 15% at 200 °C. These activities also become higher with increasing temperature.

Item Type: Conference or Workshop Item (Poster)
Subjects: Q Science > QD Chemistry
Divisions: Faculty of Mechanical Engineering > Department of Thermal Fluids
Depositing User: Mohd Haizal Mohd Husin
Date Deposited: 17 Jul 2012 02:14
Last Modified: 28 May 2015 02:40
URI: http://eprints.utem.edu.my/id/eprint/4149
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item