Nitrogen Gas Partial Pressure Control Effects on Titanium Nitride Coating’s Thickness and Colour over Tungsten Carbide Substrate using PVD

Hashim, Hanizam and Md Nizam, Abd Rahman and Noraiham, Mohamad and Hassan, Attan and Mohd Soufhwee, Abd Rahman (2012) Nitrogen Gas Partial Pressure Control Effects on Titanium Nitride Coating’s Thickness and Colour over Tungsten Carbide Substrate using PVD. In: IDECON2012, 15-16 October 2012, Melaka.

[img] PDF (Nitrogen Gas Partial Pressure Control Effects on Titanium Nitride Coating’s Thickness and Colour over Tungsten Carbide Substrate using PVD )
Hanizam-idecon2012.pdf - Published Version
Restricted to Registered users only until 3 April 2014.

Download (255kB) | Request a copy

Abstract

Titanium nitride is preferred thin coating material in the industry due to its good mechanical properties and great gold color film over machining tools and decorative parts, respectively. Optimization of titanium nitride (TiN) thin film coating on tungsten carbide (WC) substrate using physical vapor deposition (PVD) process at nitrogen (N2) and argon (Ar) gases partial pressures ratio is still lacking. In this paper, relationship between partial pressure of N2 and coating thickness was investigated. Coating characterizations were carried out using a surface stylus-based profiler and a digital 800k USB 2.0 CCD DCAM and VIS version7 software with 50% contrast and brightness settings for thickness and color, respectively. The relationship between partial pressure and coating thickness was analyzed using a statistical software Minitab version 16. Higher TiN coating thickness and better gold color appearance obtained at lower N2/Argon partial pressure ratio of 0.12 compared to 0.26. The polynomial regression equation of its relationship showed a high confident level of more than 95% and P value of 0.011. The results showed good agreement with previous works. It can be used as an indicator to determine the optimum partial pressure and indirectly represent the coating quality.

Item Type: Conference or Workshop Item (Paper)
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Divisions: Faculty of Engineering Technology > Department of Manufacturing Engineering Technology
Depositing User: HANIZAM HASHIM
Date Deposited: 19 Apr 2013 03:06
Last Modified: 28 May 2015 03:46
URI: http://eprints.utem.edu.my/id/eprint/7080
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item