The effects of bonding temperature and surface roughness on the shear strength of bonded aluminium laminates using polypropylene based adhesive

Ng, Lin Feng and Dhar Malingam, Sivakumar and Subramaniam, Kathiravan and Woo, Xiu Juan and Siva, Irulappasamy (2019) The effects of bonding temperature and surface roughness on the shear strength of bonded aluminium laminates using polypropylene based adhesive. Journal of Advanced Manufacturing Technology, 13 (2). pp. 113-127. ISSN 1985-3157

[img] Text
JAMT NG.PDF

Download (1MB)

Abstract

The high strength to weight ratio behaviour of aluminium alloys is particularly attractive in the transportation field to reduce the energy consumption. In this study, the effects of bonding temperature and the surface roughness on the single lap shear of bonded aluminium 5052 were studied. The bonding temperatures were in the range of 140°C to 170°C at an interval of 15°C whereas the surface roughness values were at 0.24, 0.49, 0.60 and 0.98. The bonded aluminium sheets were fabricated through the hot compression method in which the adhesives were located between the aluminium sheets. Single lap shear test was conducted at room temperature with reference to ASTM D1002. The results demonstrated that the bonding temperature and surface roughness of aluminium sheets influenced the lap shear strength. The aluminium with surface roughness value of 0.98 evidenced the highest shear strength regardless of bonding temperatures. When comparing the shear strength of aluminium laminates with different bonding temperature, aluminium with 170°C attested a slightly higher shear strength compared to 155°C and 140°C. The shear strength of aluminium with bonding temperature of 170°C was 0.71% and 9.81% higher than 155°C and 140°C respectively at surface roughness value of 0.98.

Item Type: Article
Uncontrolled Keywords: Metal laminates, Shear strength, Aluminium, Surface roughness, Bonding temperature
Divisions: Faculty of Mechanical Engineering
Depositing User: Sabariah Ismail
Date Deposited: 30 Jul 2020 16:24
Last Modified: 26 Jun 2023 11:20
URI: http://eprints.utem.edu.my/id/eprint/24260
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item