T6 Heat Treatment Optimization Of Thixoformed LM4 Aluminium Alloy Using Response Surface Methodology

Hashim, Hanizam and Salleh, Mohd Shukor and Abd Rahman, Mohd Soufhwee and Yahaya, Saifudin Hafiz and Abd Rashid, Mohd Warikh and Omar, Mohd Zaidi and Al-Zubaidi, Salah and Sulong, Abu Bakar (2020) T6 Heat Treatment Optimization Of Thixoformed LM4 Aluminium Alloy Using Response Surface Methodology. Malaysian Journal on Composites Science and Manufacturing, 3 (1). pp. 1-13. ISSN 2716-6945

[img] Text
915-ARTICLE TEXT-5985-1-10-20201003.PDF

Download (1MB)

Abstract

Aluminium alloy of LM4 is abundantly utilized in automotive and aerospace industries because of its good fluidity, high mechanical strength, good wear resistance and low density. T6 heat treatment as part of its forming process will enhanced further these properties. However, the total time required for T6 is very long and often delay the overall production cycle time. Furthermore, thixoforming of semi-solid processing method, which promises a near-net-shape and further enhanced performance of the end products. One of the major concerns is an additional cost in billet feedstock production that slows down the application in industries. Therefore, this paper aim is to optimize the T6 heat treatment on the thixoformed LM4 alloy using response surface methodology (RSM) of Design Expert software. Thus, a simple cooling slope casting to produce the feedstock for thixoforming of near globular and fine α-Al microstructure is being applied.Cooling slope parameters at pouring temperature of 660 °C; slope length of 440 mm and tilt angle of 45 °. As results, small globular grain size of 35.709 µ and shape factor of 0.89 are obtained. Moreover, based on the RSMM responses, the optimum parameters of T6 heat treatment; solution treatment at 530 °C for 30 minutes and 2 hours of ageing at 180 °C. The overall strength of LM4 improved significantly with ultimate tensile strength (UTS) of 252.3 MPa, 98.9 HV surface hardness and coefficient of friction (CoF) of 0.4299, respectively

Item Type: Article
Uncontrolled Keywords: Semisolid Metal Processing, Cooling Slope Casting, Aluminium Alloy, T6 Heat Treatment
Divisions: Faculty of Mechanical and Manufacturing Engineering Technology > Department of Manufacturing Engineering Technology
Depositing User: Norfaradilla Idayu Ab. Ghafar
Date Deposited: 23 Jul 2021 18:18
Last Modified: 23 Jul 2021 18:18
URI: http://eprints.utem.edu.my/id/eprint/25090
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item