Effect of CO2 Flow Rate on the Synthesis Nanosized Precipitated Calcium Carbonate, PCC

Omar, Nooririnah and Azhari, Muhammad azwar and Yusuf, Yusliza (2013) Effect of CO2 Flow Rate on the Synthesis Nanosized Precipitated Calcium Carbonate, PCC. Applied Mechanics and Materials. pp. 72-75. ISSN 1660-9336

[img] Microsoft Word
ISQNM_2013.docx - Published Version
Restricted to Registered users only

Download (14kB)

Abstract

Abstract. The precipitated of calcium carbonate has attractedmuch attention because of its numerous applications in various areas of plastics, textiles, rubbers, adhesives, paints and wastewater treatment. Nanosized of precipitated calcium carbonate,(PCC) will enhance the properties and give better performance. Its high purity and close controlled particle size and shape are making it the white filler of choice. Nanosized precipitated calcium carbonate particles were prepared using spraying method. The particles were prepared using three (3) different concentrations of Calcium Hydroxide,Ca(OH)2, three (3) CO2 flow rate and three (3) different calcinations temperature. The three (3) concentration of Calcium Hydroxide that been used are 25g/200ml, 25g/ 400ml and 25g/800ml and each of these initial solution sprayed at three (3) different CO2 flow rate, 5l/per-minute, 7l/per-minute and 10l/per-minute. Calcium Carbonate,CaCO3 powders were then calcined at three (3) different temperature, 1100°C,1200°C and 1300°C. Images from SEM showed morphology of the particles changed to spindle-like or prismatic when the ionic strength of the Calcium Hydroxide,Ca(OH)2 was increased.

Item Type: Article
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Faculty of Engineering Technology > Department of Manufacturing Engineering Technology
Depositing User: NOOR IRINAH OMAR
Date Deposited: 23 May 2014 04:18
Last Modified: 28 May 2015 04:25
URI: http://eprints.utem.edu.my/id/eprint/12433
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item