EFFECT OF AGING TREATMENT ON THE MICROSTRUCTURES AND HARDNESS OF Fe-Ni-Cr SUPERALLOY

Ridhwan, J. and Zulfattah, Z. and Selamat, Mohd Zulkefli and Hafidzal, M.H.M (2013) EFFECT OF AGING TREATMENT ON THE MICROSTRUCTURES AND HARDNESS OF Fe-Ni-Cr SUPERALLOY. International Journal of Automotive and Mechanical Engineering, 8 (1). pp. 1430-1411. ISSN 2180-1606

[img]
Preview
PDF
Effect_of_Aging_Treatment_on_the_Microstructure_and_Hardness_of_Fe-Ni-Cr_Supearalloy.pdf - Published Version

Download (655kB)
Official URL: http://ijame.ump.edu.my/

Abstract

Aging treatment was conducted on Fe-Ni-Cr superalloy to observe its effect on the microstructures and hardness of the material. Solution treatments were carried out at 900oC, 975oC, 1050oC, and 1125oC followed by water quenching. The samples were further treated with a double aging treatment at 720oC and 650oC for 4 hours and 12 hours respectively. Materials characterization techniques such as SEM, XRD, and optical microscopy were used to analyze the heat-treated samples. The Fe-Ni-Cr superalloy formed mainly a dendritic austenitic structure with Cr23C6 precipitated along the grain boundaries. Increase in solution treatment temperature results in dissolution of chromium carbide, coarser grain, and lower hardness for non-aged samples. Double aging treatment produced more chromium carbide, higher hardness, but no apparent change in grain size. Neither quenching nor aging treatments caused any phase transformation. The highest hardness value of 220.4 Hv was recorded for the sample solution treated at 1125oC for 2 hours and water quenched, followed by 2-step aging at temperature 720oC and 650oC for 4 hours and 12 hours respectively, and air cooled.

Item Type: Article
Uncontrolled Keywords: Heat treatment, aging, Fe-Ni-Cr superalloy
Subjects: Q Science > Q Science (General)
T Technology > TJ Mechanical engineering and machinery
Divisions: Faculty of Mechanical Engineering > Department of Structure and Materials
Depositing User: ENGR RIDHWAN JUMAIDIN
Date Deposited: 26 May 2014 04:17
Last Modified: 28 May 2015 04:25
URI: http://eprints.utem.edu.my/id/eprint/12524
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item