Microstructural Morphology Of Rheocast A319 Aluminium Alloy

Ahmad Muhammad, Aziz and Mohd Zaidi, Omar and Zainuddin, Sajuri and Mohd Shukor, Salleh (2016) Microstructural Morphology Of Rheocast A319 Aluminium Alloy. Advances In Mechanical Engineering, 8 (5). pp. 1-10. ISSN 1687-8132

[img] Text
Microstructural Morphology Of Rheocast A319 Aluminium Alloy.pdf - Published Version

Download (3MB)

Abstract

This article examines the evolution of the microstructure of A319 aluminium alloy as it flows along a cooling slope plate and discusses the type and influence of the intermetallic compounds thus formed. Numerous past research studies have analysed the microstructural transformation of alloys in a mould, but few researchers have investigated this phenomenon on the cooling slope plate. A change in the microstructure of the alloy from dendritic to non-dendritic is clearly obtained as the alloy moves from the impact zone to bottom zone on the cooling slope plate. It is important to clarify the mechanism of microstructural evolution through nucleation and fragmentation of the primary phase arm for fundamental understanding of research. Analysis by optical microscope and scanning electron microscope reveals the evolution of the microstructure and intermetallic compounds of A319 as it progresses along the cooling slope plate. The Vickers test was used to determine the hardness of the alloy thus produced. The results show the influence of the mould in obtaining a spheroidal microstructure; the microstructure in the bottom zone of the cooling slope plate is nearly spheroidal rather than fully spheroidal. The hardness of the alloy is enhanced when the microstructure is spheroidal and when the Mg2Si compound is present in the alloy.

Item Type: Article
Uncontrolled Keywords: Semi-solid processing, cooling slope, nucleation, evolution, intermetallic compound
Subjects: T Technology > T Technology (General)
Divisions: Faculty of Manufacturing Engineering > Department of Manufacturing Process
Depositing User: Mohd Hannif Jamaludin
Date Deposited: 27 Sep 2016 00:32
Last Modified: 12 Sep 2021 03:16
URI: http://eprints.utem.edu.my/id/eprint/17229
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item