Characteristics of A1Si7Mg0.3/X-GNPs composites manufactured via stir casting method

Salleh, Mohd Shukor and Wakhi Anuar, Nur Farah Bazilah and Yahaya, Saifudin Hafiz and Omar, Mohd Zaidi and Ali, Mohd Azamuddin and Subramonian, Sivarao (2022) Characteristics of A1Si7Mg0.3/X-GNPs composites manufactured via stir casting method. Journal Of Advanced Manufacturing Technology (JAMT), 16 (2). pp. 29-40. ISSN 1985-3157

Text 0240707062023199.PDF Download (1MB)

Abstract

Significant progress in graphene research has diverted interest to an emerging class of aluminium-based metal matrix composites. AlSi7Mg0.3 matrix composites reinforced with graphene nanoplatelets (GNPs) were fabricated via the stir casting technique. GNPs in varying amounts (0, 0.3, 0.5, 1.0 wt.%) were incorporated into the AlSi7Mg0.3 alloy via a mechanical stirring technique. Optical microstructures further analyzed the developed composites to discuss the microstructure evolution of alloys and composites. The hardness test was conducted to determine the strength of developed composites and supported by differential scanning calorimetry and X-ray diffraction. The results reveal the dendritic microstructure was decreased in the composites after adding various amounts of GNPs. The Vickers hardness value is significantly increased compared to as-cast alloy and the maximum hardness value (85.55 HV) was obtained for the AlSi7Mg0.3/0.3 wt.% GNPs. The outcomes demonstrate that incorporating a sufficient amount of GNPs into the AlSi7Mg0.3 alloy improves the hardness of the composite

Item Type:	Article
Uncontrolled Keywords:	AlSi7Mg0.3 alloy, Graphene nanoplatelets, Stir casting, Hardness
Divisions:	Faculty of Manufacturing Engineering
Depositing User:	Norfaradilla Idayu Ab. Ghafar
Date Deposited:	16 Jan 2024 10:40
Last Modified:	16 Jan 2024 10:40
URI:	http://eprints.utem.edu.my/id/eprint/27037
Statistic Details:	View Download Statistic

Actions (login required)

View Item