Morphological and wear behavior of low temperature thermochemical gaseous nitriding process

Paijan, Lailatul Harina and Maleque, Md. Abd. (2023) Morphological and wear behavior of low temperature thermochemical gaseous nitriding process. Jurnal Tribologi, 36. pp. 57-69. ISSN 2289-7232

Text 026482803202349.pdf Download (612kB)

Abstract

In this study, the nitride layer based on incorporation of nitrogen diffusion via low temperature thermochemical nitriding process were prepared. Nitriding temperature, holding time and gas flow rate during nitriding process were used as the parameters to assess morphology and wear behavior. Nitriding holding time was varying for 4, 8 and 12 hours, meanwhile temperature and glass flow rate were keeping constant. The thickness and hardness of nitride layer varied with the holding time with the thickest layer of 60.5 µm and surface hardness of 513.3 HV0.5. The nitride layers, containing expanded austenite, Fe3N and CrN phases were developed during low temperature thermochemical gas nitriding process. The expanded austenite formation on the nitride layers demonstrates that the best wear behavior is due to the highest hardness. The wear rate improved to 40 % and CoF to 23 % as compared to untreated DSS, respectively. Furthermore, it was revealed that the worn surface showed a mild ploughing and striation of wear for the nitrided samples compared to untreated DSS which demonstrated ploughing and deeper grooves. It was demonstrated that nitriding process is capable and feasible to produce hard surface layer on DSS with higher hardness and wear resistance properties.

Item Type:	Article
Uncontrolled Keywords:	Thermochemical, Nitriding, Morphological, Hardness, Wear resistance
Divisions:	Faculty Of Mechanical Technology And Engineering
Depositing User:	Norfaradilla Idayu Ab. Ghafar
Date Deposited:	06 Jan 2025 09:53
Last Modified:	06 Jan 2025 09:53
URI:	http://eprints.utem.edu.my/id/eprint/28111
Statistic Details:	View Download Statistic

Actions (login required)

View Item