Mohd Daud, Mohd Ahadlin (2009) Effect of Solution Treatment on Fatigue Properties of Magnesium Alloy. International Journal of Mechanical and Materials Engineering (IJMME), 4 (2). pp. 105-108. ISSN 1823-0334
![[img]](http://eprints.utem.edu.my/style/images/fileicons/application_pdf.png) |
PDF (Journal Scopus)
NF01[1]__IJMME_2008b.pdf Restricted to Registered users only Download (549kB) |
Abstract
The effect of solution heat treatment on fatigue properties of AZ61 magnesium alloy was investigated. The test was done by using a pneumatic fatigue testing machine under constant amplitude loading of frequency of 10 Hz. The results showed that the difference of fatigue strength for solution treated and as-extruded specimen was 30 MPa. SEM fracture surface observation showed that there were foreign particles at the crack nucleation site for solution treated specimens. The foreign particles were identified as SiC particles. However, there was no foreign particle observed on the fracture surface of the as-extruded specimen and fatigue fracture origin was relatively flat.
| Item Type: | Article |
|---|---|
| Uncontrolled Keywords: | Solution treatment, foreign particle, crack initiation, fatigue, magnesium alloy |
| Subjects: | T Technology > TJ Mechanical engineering and machinery |
| Divisions: | Faculty of Mechanical Engineering > Department of Structure and Materials |
| Depositing User: | Dr. Mohd Ahadlin Mohd Daud |
| Date Deposited: | 20 Apr 2013 13:57 |
| Last Modified: | 09 Feb 2022 10:56 |
| URI: | http://eprints.utem.edu.my/id/eprint/6802 |
| Statistic Details: | View Download Statistic |
Actions (login required)
 |
View Item |