Soft Combustion Technique: Solution Combustion Synthesis and Low-Temperature Combustion Synthesis; to Prepare Bi4Ti3O12 Powders and Bulk Ceramics

Al-Amani, Umar (2012) Soft Combustion Technique: Solution Combustion Synthesis and Low-Temperature Combustion Synthesis; to Prepare Bi4Ti3O12 Powders and Bulk Ceramics. Science of Sintering, 44. pp. 211-221. ISSN 519.718:661.887

Preview

PDF Science_of_sintering.pdf - Published Version Download (1MB)

Abstract

Bi4Ti3O12 (BTO) powders were synthesized using soft combustion techniques, specifically known as Solution Combustion Synthesis (SCS) and Low-temperature Combustion Synthesis (LCS). XRD results showed that the single phase BTO was obtained following calcinations at 800oC for the sample prepared using SCS; compared to after combustion, for the sample prepared using LCS. The TG/DTA showed a combustion temperature of around 252 - 280oC, which became stable with a single phase BTO at 500oC and above. Sintering was carried out at 1,100oC for 3 h, to determine the microstructures, grain orientation, relative density, dielectric, and ferroelectric properties, of the bulk ceramics. It was found that the bulk ceramics prepared using SCS exhibited elongated-like grains, strong (117)-preferred grain orientation, a relative density of 93.3%, εr = 320 - 360, tan δ = 0.03 - 0.1, Pr = 6.8 μC/cm2, and Ec = 20 kV/cm. Meanwhile, the bulk ceramics prepared using LCS showed plate-like grains, strong c-preferred grain orientation, a relative density of 83%, εr = 143 - 195, tan δ = 0.01 - 0.38, Pr = 5.9 μC/cm2, and Ec = 30 kV/cm.

Item Type:	Article
Subjects:	T Technology > T Technology (General)
Divisions:	Faculty of Engineering Technology > Department of Manufacturing Engineering Technology
Depositing User:	Dr. Umar Al-Amani Hj Azlan
Date Deposited:	09 Oct 2013 08:57
Last Modified:	28 May 2015 04:06
URI:	http://eprints.utem.edu.my/id/eprint/9750
Statistic Details:	View Download Statistic

Actions (login required)

View Item