Effect Of Epoxy Nozzle Separation On Die Attach Adhesion At Chip Substrate Interface

Yeo, Kian Hong (2016) Effect Of Epoxy Nozzle Separation On Die Attach Adhesion At Chip Substrate Interface. Masters thesis, Universiti Teknikal Malaysia Melaka.

[img] Text (24 Pages)
Effect of epoxy nozzle separation on die attach adhesion at chip substrate interface.pdf - Submitted Version
Restricted to Registered users only until 17 July 2021.

Download (2MB)

Abstract

Semiconductor products utilized in the automotive application need to be in high quality and more robust to ensure safe driving for the user.Thus,the semiconductor product manufacturers are moving toward zero defects target to gain the upper hand of the automotive market. One of the targets is to eliminate defects related to the die attach process.Epoxy glue void formation at the chip/substrate interface happens when multi nozzle shower is used for the glue distribution as an adhesive layer. The epoxy unable to flow uniformly,thus air is trapped in the epoxy layer at the chip/substrate interface.The current study investigates the effect of the shower head nozzles' separation (wall space) on the epoxy void formation and die shear strength.It was found that the nozzle separation has a significant and positive correlation on the void formation,but not on the shear strength of the die attach chip/substrate interface.Thus, it is recommended that the nozzles'separation (wall space) dimension to be increased by reducing quantity of nozzle used in order to reduce the void percentage to be equal or less than five percent.

Item Type: Thesis (Masters)
Uncontrolled Keywords: Nozzles,Semiconductors
Subjects: T Technology > T Technology (General)
T Technology > TK Electrical engineering. Electronics Nuclear engineering
Divisions: Faculty of Manufacturing Engineering
Depositing User: Mohd. Nazir Taib
Date Deposited: 10 Jul 2018 08:03
Last Modified: 10 Jul 2018 08:03
URI: http://eprints.utem.edu.my/id/eprint/21028
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item