Effects of DBDS and DBPC antioxidants on the corrosion of copper strips immersed in transformer oil

Sutan Chairul, Imran and Ahmad Khiar, Mohd Shahril and Ab Ghani, Sharin and Abu Bakar, Norazhar and Johal, Muhammad Syahrani and Mohamad Din, Mohamad Nazri (2024) Effects of DBDS and DBPC antioxidants on the corrosion of copper strips immersed in transformer oil. Bulletin of Electrical Engineering and Informatics, 13 (5). pp. 3043-3050. ISSN 2302-9285

[img] Text
017002007202492939916.pdf
Download (383kB)

Abstract

This paper presents the experimental findings on the effects of antioxidants on the corrosion of copper strips immersed in mineral oil (MO)–antioxidant samples. First, the uninhibited MO was mixed thoroughly with dibenzyl disulphide (DBDS) or 2,6-di-tert-butyl-p-cresol (DBPC) at different concentrations (5, 15, 25, 50, and 200 mg/kg) using a hot plate magnetic stirrer set at a temperature of 73 °C and stirring speed of 750 rpm for 15 min. Following this, the MO–antioxidant samples were poured into separate test vessels and copper strips were added into the vessels. Next, each MO– antioxidant sample was blanketed with nitrogen gas, sealed, and placed in a forced convection laboratory oven. The MO–antioxidant samples were then thermally aged at 150 °C for 48 h. The results showed that the acidity of the MO–antioxidant sample decreased with an increase in the antioxidant concentration, regardless whether the antioxidant was DBDS or DBPC. However, the corrosion of the copper strip worsened with an increase in the antioxidant concentration, where DBDS had a higher relative degree of corrositivity to copper compared with DBPC. In addition, the results showed that a DBPC concentration of 25 mg/kg reduced the the acidity of the MO– antioxidant sample and resulted in a moderate tarnish of the copper strip.

Item Type: Article
Uncontrolled Keywords: 2,6-di-tert-butyl-p-cresol, Acidity, Antioxidants, Copper corrosion, Dibenzyl disulfide
Divisions: Faculty Of Electrical Technology And Engineering
Depositing User: Sabariah Ismail
Date Deposited: 09 Oct 2024 16:32
Last Modified: 09 Oct 2024 16:32
URI: http://eprints.utem.edu.my/id/eprint/27842
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item