Formation of Cr23C6 During the Sensitization of AISI 304 Stainless Steel and its Effect to Pitting Corrosion

Mohd Warikh, Abd Rashid and Miron, Gakim and Zulkifli, Mohd Rosli and Mohd Asyadi 'Azam, Mohd Abid (2012) Formation of Cr23C6 During the Sensitization of AISI 304 Stainless Steel and its Effect to Pitting Corrosion. International Journal of Electrochemical Science (IJES), 7. pp. 9465-9477. ISSN 1452-3981

[img]
Preview
PDF
Paper_warikh.pdf - Published Version

Download (1MB)

Abstract

The metallic carbide precipitation was observed after the sensitization of AISI 304 stainless steel specimens in neutral flame by using oxy-fuel and slowly cooled in the air. Correlation between corrosion and X-Ray Diffraction (XRD) shows that the enrichment of Cr23C6 in the microstructure of AISI 304 worsens the pitting corrosion resistance properties as the sensitization time increases from 5 to 60 s. However, the precipitation dissolved and corrosion resistance properties improved after the specimens treated in solution quenching treatment at 1130 oC, soaked from 24 – 120 min, then rapidly cooled in water.

Item Type: Article
Subjects: Q Science > Q Science (General)
Divisions: Faculty of Manufacturing Engineering > Department of Engineering Materials
Depositing User: Prof. Madya Dr. Mohd. Warikh Abd. Rashid
Date Deposited: 15 Apr 2013 12:37
Last Modified: 28 May 2015 03:47
URI: http://eprints.utem.edu.my/id/eprint/7168
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item