Ti6Al4V Surface Hardness Improvement by Duplex Coating

Mohd Rosli, ZULKIFLI and yusliza, yusuf and Jariah, Mohamad Juoi and Zainab , Mahamud and Kwan, Wai Loon (2013) Ti6Al4V Surface Hardness Improvement by Duplex Coating. Advanced Materials Research. pp. 370-374. ISSN 1022-6680

PDF AMR.701.370_Yusliza.pdf Restricted to Registered users only Download (678kB)

Abstract

Ti6Al4V alloy are among the most widely used materials in engineering applications. This is because their relatively beneficial properties. However, inadequate wear properties of Ti6Al4V alloy have largely constrained the application for this material. In this study, Plasma nitriding of the Ti6Al4V was performed using microwave plasma technique at 600oC for 1hour, 3 hours and 5 hours then followed with deposition of CrN on plasma nitrided samples for duplex coating purposes. Microstructural analysis and hardness measurement revealed that formation of Ti2N and TiN phases indicating the formation of compound layer is observed for substrate nitrided at temperature as low as 600oC 1 hour and a substantial increase on the surface hardness of plasma nitrided Ti6Al4V is observed with an increase of process time. The duplex coating obtained in this study has significant surface hardness property and superior as compared with CrN coatings deposited on as received Ti6Al4V.

Item Type:	Article
Subjects:	Q Science > Q Science (General) T Technology > T Technology (General)
Divisions:	Faculty of Manufacturing Engineering > Department of Engineering Materials
Depositing User:	Dr. Zulkifli Mohd Rosli
Date Deposited:	05 Feb 2014 08:11
Last Modified:	28 May 2015 04:14
URI:	http://eprints.utem.edu.my/id/eprint/10967
Statistic Details:	View Download Statistic

Actions (login required)

View Item