Formation of Cr23C6 during the Sensitization of AISI 304 Stainless Steel and its Effect to Pitting Corrosion

A.R.M, Warikh and Mohd Rosli, ZULKIFLI and Gakim, Miron and M.A, ASYADI AZAM (2012) Formation of Cr23C6 during the Sensitization of AISI 304 Stainless Steel and its Effect to Pitting Corrosion. International Journal of Electrochemical Sience. pp. 9465-9477. ISSN 1452-3981

[img] PDF
Mohd_Asyadi_Azam_(revised120720)_2012.pdf
Restricted to Registered users only

Download (1MB)

Abstract

The metallic carbide precipitation was observed after the sensitization of AISI 304 stainless steel specimens in neutral flame by using oxy-fuel and slowly cooled in the air. Correlation between corrosion and X-Ray Diffraction (XRD) shows that the enrichment of Cr23C6 in the microstructure of AISI 304 worsens the pitting corrosion resistance properties as the sensitization time increases from 5 to 60 s. However, the precipitation dissolved and corrosion resistance properties improved after the specimens treated in solution quenching treatment at 1130 oC, soaked from 24 – 120 min, then rapidly cooled in water.

Item Type: Article
Subjects: Q Science > Q Science (General)
T Technology > T Technology (General)
Divisions: Faculty of Manufacturing Engineering > Department of Engineering Materials
Depositing User: Dr. Zulkifli Mohd Rosli
Date Deposited: 05 Feb 2014 08:15
Last Modified: 28 May 2015 04:14
URI: http://eprints.utem.edu.my/id/eprint/10974
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item